变In组分沟道的MM-HEMT材料电子输运特性研究

在变缓冲层高迁移率晶体管（MM_HEMT）器件中，二维电子气的输运性质对器件性能起着决定作用.通过低温下二维电子气横向电阻的量子振荡现象，结合变温度的Hall测量，系统研究了不同In组分沟道MM_HEMT器件中子带电子迁移率和浓度随温度的变化关系.结果表明，沟道中In组分为0.65的样品，材料电学性能最好，In组分高于0.65的样品，严重的晶格失配将产生位错，引起迁移率下降，大大影响材料和器件的性能. 关键词： 变缓冲层高迁移率晶体管 Shubnikov_de Hass 振荡     

Effect of Ultrashort Pulsed Laser and X-Ray Irradiation on Au+ -Doped Glass

Au nanoparticles were precipitated inside Au+-doped glass samples after irradiation by femtosecond laser or x-ray. Femtosecond laser and X-ray irradiation result in decreasing of anneal temperature and critical size for the precipitation of Au nanoparticles.     

关于无界无限维商品空间上的生产经济均衡

本文研究了无界无限维商品空间上的生产经济均衡的存在性．虽然我们把商品空间看成是Ｒｉｅｓｚ空间，但并没有在它的正锥上作任何内部假设．同时我们的结果也为现代企业或公司从事经济预测、制订生产计划、改善经营管理、提高劳动生产率以及优化经济机制提供了理论依据．     

高效蛋白质浓缩剂的制备及浓缩作用的研究

采用自由基水溶液聚合方法合成了超高分子量的丙烯酸（钠）聚合物。该聚合物具有高达几十倍至上千倍的吸水能力，通过适当控制聚合物的交联度使其成为具有一定孔径的网状物，可用于生物大分子，如：蛋白质溶液或其它生物提取液的浓缩。试验了用反透析法浓缩胰蛋白酶的方法，与直接加入浓缩法相比，能够更好地保持酶的活性。与传统的浓缩方法相比，用该方法浓缩蛋白质具有效率高，浓缩剂用量少的优点。     

非本征型法布里-珀罗干涉仪光纤布拉格光栅应变温度传感器及其应用

介绍了光纤布拉格光栅非本征型法布里珀罗干涉仪集成复用传感器的结构、应变和温度同时监测的原理 ;观察到光纤布拉格光栅反射谱和非本征型法布里珀罗干涉仪干涉谱间的串扰 ,用 3dB带宽平均波长法减小了该串扰 ,提高了测量精度 ;将该传感器应用于三维编织复合材料的应变及温度同时监测。实验结果表明温度精度为± 1℃ ,应变精度为± 2 0 μ ,可满足实际应用的要求     

钾离子选择电极及其在生物医学中的应用进展

钾离子选择电极的研究一直是一个非常活跃的题目,具有令人瞩目的发展。本文就其研制、测试法与应用方面的新进展进行评述。     

非晶态硒化镉薄膜瞬态光电特性

本文报道用真空热蒸发法淀积的非晶态硒化镉薄膜作光敏介质制备超快光电导探测器。用对撞脉冲锁模Nd:YAG激光器产生的超短光脉冲序列对探测器的响应时间进行检测,结果表明a-CdSe薄膜对皮秒(10^-12秒)级的超短光脉冲作用具有良好的瞬态响应光电特性,探讨a-CdSe薄膜快速弛豫过程的内在机理。     

YZr2OZr3:Er3+纳米晶anti-Stokes发光性质的研究

采用均相沉积法制备了不同Er³⁺离子浓度掺杂的Y₂O₃纳米晶, 应用XRD，SEM和PL光谱对该体系材料进行了表征.在Y₂O₃:Er³⁺纳米材料体系中, 观察和研究了Stokes及anti-Stokes PL谱强度与Er³⁺离子摩尔浓度变化的关系, 当Er³⁺离子浓度为2.0mol%时, anti-Stokes PL强度最强.粉末X 关键词： 氧化钇纳米晶 anti-Stokes PL 双光子吸收     

Studies on the chemical constituents of the South China Sea sponge Phacellia fusca

Three pyrrololactam alkaloids have been isolated from the marine sponge Phacellia fusca Schmidt collected from the South China Sea, and their structures were determined as 1–3 , on the grounds of spectral data. This is the first report of these compounds from this sponge. The structure of 1 was confirmed by X-ray analysis.     

Thermal Behavior of Urea-(D) Tartaric Acid and Urea-(DL) Tartaric Acid Crystals

The thermal behavior of two new non-linear optical (NLO) materials, urea-(D) tartaric acid (UDT) and urea-(DL) tartaric acid (UDLT) were studied by using DSC, TG and TMA. The results show that: 1) The two crystals have different melting points but similar decomposition temperatures due to the influences of intermolecular forces, which is attributed to the stereo effects of (D)-tartaric and (DL)-tartaric acid molecules; 2) There was only thermal expansion and no thermal contraction when the UDT and UDLT crystals were heated; 3) There was no phase transition within the measured temperature range; 4) The thermal expansion of the UDT and UDLT crystals shows a small anisotropy; 5) The specific heats of UDT and UDLT change linearly with temperature in the measured temperature range and the value for UDT is 1.321 J g-1 K-1 at 320 K while the specific heat of UDLT is 1.357 J g-1 K-1 at the same temperature. This revised version was published online in July 2006 with corrections to the Cover Date.